Butenko, A. F.Sergeeva, A. E.Soloshenko, Viktor I.Fedosov, S. N.Бутенко, А. Ф.Сергєєва, О. Є.Солошенко, Віктор ІвановичФедосов, С. Н.Бутенко, А. Ф.Сергеева, А. Е.Солошенко, Виктор ИвановичФедосов, С. Н.2010-09-102010-09-102006Фотоэлектроника = Photoelectronicshttps://dspace.onu.edu.ua/handle/123456789/280Фотоэлектроника = Photoelectronics / ОНУ имени И. И. Мечникова. - Одесса : Астропринт, 2006.Thermally stimulated polarization and depolarization currents in composite materials made of polyvinylidenefluoride (PVDF) and BaTiO3 ceramics are studied experimentally. It has been found that the decrease in conductivity is related to the formation of the ferroelectric polarization. The information on parameters of the relaxation processes is obtained by the Relaxation Map Analysis (RMA) method. The experimental results are consistent with the model of the polari- zation development in ferroelectric polymers. Експериментально вивчені струми термостимульованої поляризації (ТСП) і деполяризації (ТСД) композиційних матеріалів на основі полівініліденфториду (ПВДФ) і порошку ВаТiО3. Встановлено, що зменшення провідності композитів пов'язано з формуванням в них сегнетоелектричної поляризації. Методом термічних вікон (МТВ) отримані дані про параметри релаксаційних процесів. Експериментальні результати знаходяться у відповідності з моделлю формування поляризації в сегнетоелектричних полімерах. Экспериментально изучены токи термостимулированной поляризации (ТСП) и деполяризации (ТСД) композиционных материалов на основе поливинилиденфторида (ПВДФ) и порошка ВаТiО3. Установлено, что уменьшение проводимости композитов связано с формированием в них сегнетоэлектрической поляризации. Методом термических окон (МТО) получены данные о параметрах релаксационных процессов. Экспериментальные результаты находятся в соответствии с моделью формирования поляризации в сегнетоэлектрических полимерах.enArticle